ive only done about 2 1/2 weeks on TIG but i thought it looked pretty good. what do you guys think?

 

 

Hard to tell from that angle but looks alittle undercut, not bad though

 

keep on tigging

 

Yeah, i agree it looks a little concave. What size filler rod are you using? From the looks of that bead im guessing you are using either too much heat or a 1/16" filler rod. If you are only using 1/16" step up to 3/32" its way better for welds like that.

 

yup.......only had 1/16 on hand. this was just practice as ive never done tig before just used whatever there was laying around......hence the shitty plates i used.

 

Dood keep up the good work! How is the schoolin goin? Anywho keep on keepin on. And if I ever go FI, that Ti manifold will be sweet.

 

thanks bro........always nice hearin from ya. school going good how about you?